LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Powder for High Power Li-ion Battery Cathode, 200g/bottle-EQ-Lib-LNCM622
LiNiCoMnO2 (Lithium Nickel Manganese Cobalt Oxide) powder for Li-ion battery cathode, 200g/bottle (Ni : Co : Mn = 6 : 2 : 2, NCM622 or NMC622).
Specification
| Properties | Item | Measured Value | Standard Value | |
|
Chemical Composition |
Li (Wt%) | 7.2±0.6 | 7.4 | |
| Ni+Co+Mn (Wt%) | 59.0±1.0 | 58.6 | ||
|
Impurities |
Na (ppm) |
≤100 |
20 | |
| Fe (ppm) |
≤100 |
30 | ||
| Cu (ppm) |
≤50 |
1 | ||
|
Size Distribution |
D10 (μm) |
≥5.0 |
6.6 | |
| D50 (μm) |
11±2 |
11.0 | ||
| D90 (μm) |
≤28 |
18 | ||
|
Dmax(μm) |
≤45 | 28.9 | ||
| Specific Surface Area (m2/g) | 0.35±0.15 | 0.27 | ||
| Tap Density (g/cm³) | ≥2.1 | 2.65 | ||
|
Electrochemical Properties |
Discharge specific capacity | ≥5.0 | 176.0 | |
| First charge and discharge efficiency (%) | ≥85.0 | 89 | ||
| SDS |
 |
|||
Note: MTI does not manufacture this product, and only sells a small quantity to research for the development of new generation batteries. If you need a larger quantity or have a question about the IP, we will forward your inquiry to the producer.
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
Related Products
 Vacuum Storage Box |
 Powder Milling & Mixer |
 Electrode Coaters |
 Battery Research Equipment |
 Other Battery Powders |
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
LiNiCoMnO2 (Lithium Nickel Manganese Cobalt Oxide) powder for Li-ion battery cathode, 200g/bottle (Ni : Co : Mn = 6 : 2 : 2, NCM622 or NMC622).
Specification
| Properties | Item | Measured Value | Standard Value | |
|
Chemical Composition |
Li (Wt%) | 7.2±0.6 | 7.4 | |
| Ni+Co+Mn (Wt%) | 59.0±1.0 | 58.6 | ||
|
Impurities |
Na (ppm) |
≤100 |
20 | |
| Fe (ppm) |
≤100 |
30 | ||
| Cu (ppm) |
≤50 |
1 | ||
|
Size Distribution |
D10 (μm) |
≥5.0 |
6.6 | |
| D50 (μm) |
11±2 |
11.0 | ||
| D90 (μm) |
≤28 |
18 | ||
|
Dmax(μm) |
≤45 | 28.9 | ||
| Specific Surface Area (m2/g) | 0.35±0.15 | 0.27 | ||
| Tap Density (g/cm³) | ≥2.1 | 2.65 | ||
|
Electrochemical Properties |
Discharge specific capacity | ≥5.0 | 176.0 | |
| First charge and discharge efficiency (%) | ≥85.0 | 89 | ||
| SDS |
|
|||
Note: MTI does not manufacture this product, and only sells a small quantity to research for the development of new generation batteries. If you need a larger quantity or have a question about the IP, we will forward your inquiry to the producer.
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.